| عنوان فارسی مقاله | Effect of Various Laser Surface Treatments on Repair Shear Bond Strength of Aged Silorane-Based Composite |
| عنوان لاتین مقاله | Effect of Various Laser Surface Treatments on Repair Shear Bond Strength of Aged Silorane-Based Composite |
| ناشر | 7 |
| آیا مقاله از طرح تحقیقاتی و یا منتورشیپ استخراج شده است؟ | بلی |
| عنوان نشریه (خارج از لیست فوق) | |
| نوع مقاله | Original Article |
| نحوه ایندکس شدن مقاله | ایندکس شده سطح دو – PMC |
| آدرس لینک مقاله/ همایش در شبکه اینترنت | https://www.ncbi.nlm.nih.gov/pubmed/29071025 |
| Abstract Introduction: Successful repair of composite restorations depends on a strong bond between the old composite and the repair composite. This study sought to assess the repair shear bond strength of aged silorane-based composite following surface treatment with Nd:YAG, Er,Cr:YSGG and CO2 lasers. Methods: Seventy-six Filtek silorane composite cylinders were fabricated and aged by 2 months of water storage at 37°C. The samples were randomly divided into 4 groups (n=19) of no surface treatment (group 1) and surface treatment with Er,Cr:YSGG (group 2), Nd:YAG (group 3) and CO2 (group 4) lasers. The repair composite was applied and the shear bond strength was measured. The data were analyzed using one-way analysis of variance (ANOVA) and Tukey posthoc test. Prior to the application of the repair composite, 2 samples were randomly selected from each group and topographic changes on their surfaces following laser irradiation were studied using a scanning electron microscope (SEM). Seventeen other samples were also fabricated for assessment of cohesive strength of composite. Results: The highest and the lowest mean bond strength values were 8.99 MPa and 6.69 MPa for Er,Cr:YSGG and control groups, respectively. The difference in the repair bond strength was statistically significant between the Er,Cr:YSGG and other groups. Bond strength of the control, Nd:YAG and CO2 groups was not significantly different. The SEM micrographs revealed variable degrees of ablation and surface roughness in laser-treated groups. Conclusion: Surface treatment with Er,Cr:YSGG laser significantly increase the repair bond strength of aged silorane-based composite resin. |
| نویسنده | نفر چندم مقاله |
|---|---|
| پرنیان علیزاده اسکویی | اول |
| سیاوش سوادی اسکویی | دوم |
| سهند ریخته گران | سوم |
| فاطمه پورنقی آذر | چهارم |
| نام فایل | تاریخ درج فایل | اندازه فایل | دانلود |
|---|---|---|---|
| jlms-8-186.pdf | 1396/11/24 | 1265138 | دانلود |