| عنوان فارسی مقاله | Effect of preheat repetition on color stability of methacrylate- and silorane-based composite resins |
| عنوان لاتین مقاله | Effect of preheat repetition on color stability of methacrylate- and silorane-based composite resins |
| ناشر | 7 |
| آیا مقاله از طرح تحقیقاتی و یا منتورشیپ استخراج شده است؟ | بلی |
| عنوان نشریه (خارج از لیست فوق) | - |
| نوع مقاله | Original Article |
| نحوه ایندکس شدن مقاله | ایندکس شده سطح دو – PubMed |
| آدرس لینک مقاله/ همایش در شبکه اینترنت | https://www.ncbi.nlm.nih.gov/pubmed/?term=Effect+of+preheat+repetition+on+color+stability+of+methacrylate-+and+silorane-based+co |
| Background. The aim of this study was to investigate the effect of preheating methacrylate- and silorane-based composite resins on their color stability up to 40 times at 55‒60°C. Methods. Seventy-six methacrylate and silorane-based composite resin samples, with a diameter of 10 mm and a height of 2 mm, were divided into 4 groups (n=19). After the samples were prepared, their color parameters were determined using a reflective spectrophotometer. The composite resin samples were separately stored in a solution of tea for 40 consecutive days. Then the samples underwent a color determination procedure again using a spectrophotometer and color changes were recorded. Finally two-way ANOVA was used to study the effect of composite temperature on its staining (P<0.05). Independent-samples t-test was used to evaluate changes in conversion rates of preheated composite resin samples compared to non-heated samples at P=0.005 and P=0.029 for silorane-based and Z250 composite resin samples, respectively. Results. Both composite resin type (P=0.014) and preheating (P<0.001) had significant effects on ΔE. Conclusion. Repeated preheating of methacrylate- and silorane-based composite resin samples, up to 55‒60°C for 40 rounds, resulted in more color changes compared with unheated composite resin samples. After storage in a solution of tea the color change rate in the composite resin samples of silorane-based was higher than the Z250 composite resin samples. |
| نویسنده | نفر چندم مقاله |
|---|---|
| مهدی عابد کهنمویی | اول |
| سهند ریخته گران | سوم |
| مهدی دانشپوی | چهارم |
| سودابه کیمیائی | پنجم |
| پرنیان علیزاده اسکویی | ششم |
| یاشار رضاعی | هفتم |
| نام فایل | تاریخ درج فایل | اندازه فایل | دانلود |
|---|---|---|---|
| Kahnamoeei.pdf | 1396/10/26 | 211939 | دانلود |