| عنوان فارسی مقاله | The Effect of Thickness on the Sealing Ability of CEM Cement as a Root-end Filling Material. |
| عنوان لاتین مقاله | The Effect of Thickness on the Sealing Ability of CEM Cement as a Root-end Filling Material. |
| ناشر | 6 |
| آیا مقاله از طرح تحقیقاتی و یا منتورشیپ استخراج شده است؟ | خیر |
| عنوان نشریه (خارج از لیست فوق) | JODDD |
| نوع مقاله | Original Article |
| نحوه ایندکس شدن مقاله | ایندکس شده سطح دو – PubMed |
| آدرس لینک مقاله/ همایش در شبکه اینترنت | http://www.ncbi.nlm.nih.gov/pmc/articles/PMC4417497/ |
| Background and aims. Different materials have been used for root-end filling during surgical endodontic treatment. The aim of this in vitro study was to evaluate the dye penetration in different thicknesses of calcium enriched mixture (CEM) cement as root-end filling material. Materials and methods. Following root canal filling in 70 extracted human single-rooted premolar teeth, the apical 3 mm of their root-ends was resected; the root-end cavities with depths of 1, 2 and 3 mm were prepared by ultrasonic retrotips and filled with CEM cement. After setting of cement, the roots were immersed in 2% Rhodamine B and the dye leakage was measured under stereomicroscope (×16) using Image J software. The data were analyzed by one-way ANOVA and Bonferroni post hoc tests at 5% significance level. Results. The means and standard deviations of dye penetration in the 1, 2, and 3 mm groups were 3395.5±1893.4, 3410.4±1440.5, and 2581.6±1852.9 μm, respectively. The one-way ANOVA analysis indicated significant differences (P < 0.001); however, the Bonferroni post hoc test revealed that only the positive control group differed significantly from the experimental groups (P < 0.001). Conclusion. The findings demonstrated CEM cement to have an adequate root-end sealing ability in 3-mm thickness. |
| نویسنده | نفر چندم مقاله |
|---|---|
| سعید رحیمی دره چی | اول |
| محمد سمیعی | سوم |
| محمود بهاری | چهارم |
| نام فایل | تاریخ درج فایل | اندازه فایل | دانلود |
|---|---|---|---|
| joddd-9-6.pdf | 1395/03/23 | 72825 | دانلود |